D212耐磨堆焊焊條

聯系該企業時請說明您是在《制冷名錄》看到該信息,以獲得更多的信任和更好的服務。
價格:23.00/公斤
進店看看>
上海馳進焊材有限公司
  • 聯系人:李書娥
  • 點擊獲取聯系方式
  • 地區:上海
產品分類
熱銷產品

D212

符合 GB EDPCrMo-A4-03

25/kg
說明: D212是鈦鈣型藥皮的CrMo型堆焊焊條,可交直流兩用。堆焊時電弧穩定,脫渣容易。


用途:用于單層或多層堆焊各種受磨損的機件表面,如齒輪、挖斗、礦山機械等。


熔敷金屬化學成分(%)

化學成分

C

Mo

Cr

保證值

0.30~0.60

≤4.00

≤5.00


堆焊層硬度:
HRC≥50


參考電流
(AC、DC)

焊條直徑(mm)

φ3.2

φ4.0

φ5.0

焊接電流(A)

90~120

150~180

190~230


注意事項:
1.
焊前焊條須經150左右烘焙1h。
2.
大型工件堆焊前應適當預熱至300左右,并將堆焊部分表面的鐵銹和油污清除干凈。

 

 

好評度
{{GoodNumPer}}%
{{item.LabelTitle}}
  • 全部評價({{AppraiseStatistics.AllNum}})
  • 好評({{AppraiseStatistics.GoodNum}})
  • 中評({{AppraiseStatistics.MidNum}})
  • 差評({{AppraiseStatistics.BadNum}})
  • 曬圖
同類推薦
主站蜘蛛池模板: | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | | |